Zhongfa PA66 66G30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B1UycT_Zhongfa-PA66-66G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PA66 66G30 is a polyamide 66 (nylon 66) material, which contains a 30% glass fiber reinforced material. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of the Zhongfa PA66 66G30 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6800 | MPa | ASTM D790 |
| Flexural Strength | 240 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 240 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 14 kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 6.0 - 8.0 | hr | |
| Processing (Melt) Temp | 235 - 275 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3WG6 CR BK23210 | BASF Corporation | Nylon 6 | Ultramid® |
| Avalon 30 | Greene, Tweed & Co. | PTFE | Avalon |
| Geon™ Vinyl Flexible B5D02 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hifax TYC 1123P RXF Black | LyondellBasell Industries | TPO (POE) | Hifax |
| ULTEM™ 1000E resin | SABIC Innovative Plastics | PEI | ULTEM™ |