STAR-THERM® E A-3C
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | STAR-THERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B13F3v_STAR-THERM-E-A-3C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STAR-THERM® E A-3C is a Polyamide 66 (Nylon 66) product filled with 30% carbon fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 21000 | 16500 | MPa | |
| 90°C | 14000 | -- | MPa | |
| 120°C | 10000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break, 23°C | 260 | 200 | MPa | |
| Break, 90°C | 150 | -- | MPa | |
| Break, 120°C | 125 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19000 | 15000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 370 | 285 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 253 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.51 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+2 | -- | ohms | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Front Temperature | 285 to 310 | °C | |
| Nozzle Temperature | 285 to 320 | °C | |
| Processing (Melt) Temp | < 310 | °C | |
| Mold Temperature | 80.0 to 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aarolene® ARPE HD 300-2 | Aaron Industries Corp. | HDPE | Aarolene® |
| Akulon® K222-KGV5 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Flexathene® TP39NC01 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Fixmaster Flex 80 Liquid | Loctite® | PUR, Unspecified | Fixmaster |
| FUDOWLITE® F5980F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |