Diaterm® B26 HX
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DTR S.r.l. (Develop Thermoplastic Resins) |
| Trademark: | Diaterm® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B10Z1P_Diaterm-B26-HX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diaterm®B26 HX is a polyamide 66 (nylon 66) material,. This product is available in Europe,. Diaterm®The main features of B26 HX are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 225 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 240 | °C | ASTM D1525 1 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Water Absorption, DIN 53714, 23°C, 50% RH: 3%Burning Rate, DIN 75200: <100mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2002-4A | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Stat-Rite® S-1110 | Lubrizol Advanced Materials, Inc. | PE, Unspecified | Stat-Rite® |
| AvaSpire® AV-651 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| HAIPLEN H50 T6 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| InvisiSil™ IVS4742 | Momentive Performance Materials Inc. | Silicone | InvisiSil™ |