P-FLEX R 2620
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | P-FLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B0wkDw_P-FLEX-R-2620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS compounded with glass fiber with a high stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.25 - 0.35 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 45.0 | MPa | ISO 527-2 |
| Fracture | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 45 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 HF UV | RTP Company | PP, Unspecified | RTP |
| VENELENE® 2706 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| Toraypef® 30050 AG00 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| CGPC PVC SO-30X (105 phr Plasticizer E) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| PENTAMID B MA 25 H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |