AKROMID® C3 GF 40 1 black (4658)
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B0eYDA_AKROMID-C3-GF-40-1-black-4658-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® C3 GF 40 1 black (4658) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend. Applications are mainly components in mechanical engineering and the automotive industry where good flowability is required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.47 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 82.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.30 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.7 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 130 to 150 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 160 to 175 | -- | °C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 40 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12800 | 9100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 220 | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 12200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 330 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | 120 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 8.0 MPa, Unannealed | 215 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 260 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Technother® A-SV30-ODI | Poly Plastic | PBT | Technother® |
| Toughblend® PA66-1700 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| Daicel PP PT2N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| EnviroPro 9003 | West Michigan Compounding | PP Copolymer | EnviroPro |
| Huafon JF-HSY-ADP1 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |