P-BLEND X5
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | P-BLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B0WFuV_P-BLEND-X5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polymerblend of PC/ABS. In comparison to ABS higher impact strength and heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 46.0 | MPa | ISO 527-2 |
| Fracture | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 10 | kJ/m² | ISO 180 |
| 23°C | 23 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 46 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP553 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| RTP EMI 863 | RTP Company | Acetal (POM) Copolymer | RTP |
| LUVOCOM® NSB 90 NT | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| PPR PC03 | Premier Plastic Resins, Inc. | PC | PPR |
| ALTECH® PC ECO 2020/146 FR GF20 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |