VALOX™ 3706 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B0Q295_VALOX-3706-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified PBT+PC resin. Outdoor enclosure. Not available in all colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 1.2 to 1.4 | % | |
| Across Flow : 3.20 mm | 1.2 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1970 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 49.0 | MPa | |
| Break | 39.3 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 50 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2000 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 78.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 670 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 49.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.6E-5 | cm/cm/°C | |
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 7 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.49 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-10 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| SILVER® SA-2105 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| Ultramid® B3WG6 GPX BK23238 | BASF Corporation | Nylon 6 | Ultramid® |
| NEFTEKHIM PE 4115P (16402) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Sumiliteresin® PR-53497 | SBHPP | Phenolic | Sumiliteresin® |