Geon™ Vinyl Rigid Extrusion L7100
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B0LNGB_Geon-Vinyl-Rigid-Extrusion-L7100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon L7100 is recommended for whites and light pastel colors only. Not recommended for horizontal applications such as railing and decking except in white. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 15354 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2780 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 44.6 | MPa | ASTM D638 |
| Flexural Modulus | 3170 | MPa | ASTM D790 |
| Flexural Strength | 81.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 23°C, 3.18mm, molded 3 | 130 | J/m | ASTM D256A |
| 23°C, 3.18mm, molded 4 | 570 - 810 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C | 75.2 - 77.4 | J/cm | ASTM D4226 |
| 23°C | 77.0 - 79.2 | J/cm | ASTM D4226 |
| 23°C, 2.03 mm | 74.3 | J/cm | ASTM D4226 |
| 23°C, 2.03 mm | 111 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 75.2 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 77.6 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 7 | 72.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 8 | 75.4 | °C | ASTM D648 |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 注释：物理属性基于L7005 tan 3210 样品。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Physical property based on commercial production sample. Compression molding of extruded strips. |
| 4 . | Physical property based on lab scale production sample. |
| 5 . | Annealed at 50 deg.C |
| 6 . | Annealed at 60 deg.C |
| 7 . | Annealed at 50 deg.C |
| 8 . | Annealed at 60 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1695 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TECHNO ABS 150 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Hifax EKS 157D NAT | LyondellBasell Industries | PP, Unspecified | Hifax |
| ICORENE® 9402 | ICO Polymers EMEA, A Division of A. Schulman | TPE | ICORENE® |
| Plaskon SMT-B-1LAR | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |