AT 190
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B0CTgp_AT-190.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This resin is suitable for use in Hot Melt Adhesive, carpet extrusion, and coating applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.914 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (125°C/0.325 kg) | 70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 8.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 120 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 130 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 102 | °C | DSC |
| Additional Information |
|---|
| The value listed as Density-Specific Gravity, ASTM D1505, was also tested in accordance with ASTM D1928 ProcC Mod.Ring and Ball Softening Point: 117°C |
| Note Message | |
|---|---|
| 1 . | Type 4, 50mm/min |
| 2 . | Type 4, 50mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AZM 23 G9 T6LD | Arkema | Nylon 12 | Rilsan® |
| ProTherm® 4526 | Axiall Corporation | CPVC | ProTherm® |
| Taitacell EPS 321F | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Bergadur™ PB40 G50 BK003 | PolyOne Corporation | PBT | Bergadur™ |
| LUVOCOM® 80/TF/22/NT | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |