Lupox® SG3180S
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AzGrGk_Lupox-SG3180S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Good Surface Application Automotive(Head Lamp Bezel) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 33 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 to 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4020 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 94.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 195 | °C | ASTM D648 |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 301MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| WPP PP PPC4TF1.3-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Gallonprene® GP420-9007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Lupoy® 3030-10 | LG Chem Ltd. | PC | Lupoy® |
| LNP™ THERMOTUF™ MF004AI compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOTUF™ |