Generic Phenolic - Glass Fiber
| Category: | Phenolic , Phenolic |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AyzGKR_Generic-Phenolic---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Phenolic - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.68 - 2.01 | g/cm³ | ASTM D792 |
| 23°C | 1.60 - 2.01 | g/cm³ | ISO 1183 |
| Apparent Density | |||
| -- | 0.70 - 0.81 | g/cm³ | ASTM D1895 |
| -- | 0.62 - 0.81 | g/cm³ | ISO 60 |
| Bulk Factor | 2.0 - 3.0 | ASTM D1895 | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.098 - 0.31 | % | ASTM D955 |
| 23°C | 0.038 - 0.37 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 - 0.12 | % | ASTM D570 |
| 23°C, 24 hr | 0.020 - 0.16 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 80 - 125 | ASTM D785 | |
| 23°C | 79 - 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2.70 - 17200 | MPa | ASTM D638 |
| 23°C | 12800 - 18000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 34.9 - 65.7 | MPa | ASTM D638 |
| Fracture, 23°C | 44.9 - 131 | MPa | ISO 527-2 |
| 23°C | 32.0 - 138 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 0.60 - 0.81 | % | ASTM D638 |
| Fracture, 23°C | 0.54 - 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8660 - 17600 | MPa | ASTM D790 |
| 23°C | 9800 - 20000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 72.9 - 190 | MPa | ASTM D790 |
| 23°C | 88.5 - 186 | MPa | ISO 178 |
| Yield, 23°C | 73.6 - 170 | MPa | ASTM D790 |
| Compressive Strength | |||
| 23°C | 161 - 293 | MPa | ASTM D695 |
| 23°C | 166 - 314 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 19.1 - 99.3 | J/m | ASTM D256 |
| 23°C | 3.2 - 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 9.8 - 21 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 6.9 - 66 | J/m | ASTM D256 |
| 23°C | 2.4 - 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 180 - 320 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 177 - 287 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 282 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 136 - 250 | °C | ISO 75-2/C |
| Continuous Use Temperature | 180 - 236 | °C | ASTM D794 |
| Linear thermal expansion coefficient | |||
| Flow | 1.1E-5 - 3.8E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.2E-5 - 3.9E-5 | cm/cm/°C | ASTM E831 |
| Flow | 5.0E-6 - 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.7E-5 - 4.5E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (23°C) | 0.34 - 0.81 | W/m/K | ASTM C177 |
| RTI Elec | 150 - 180 | °C | UL 746 |
| RTI Imp | 150 - 151 | °C | UL 746 |
| RTI | 150 - 151 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 - 2.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 4.0E+9 - 1.0E+13 | ohms·cm | ASTM D257 |
| 23°C | 4.0E+9 - 7.6E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 7.9 - 17 | kV/mm | ASTM D149 |
| 23°C | 9.7 - 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 4.97 - 6.31 | ASTM D150 | |
| 23°C | 4.30 - 5.50 | ASTM D2520 | |
| Dissipation Factor (23°C) | 0.010 - 0.044 | ASTM D150 | |
| Arc Resistance | 178 - 191 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 - 200 | V | UL 746 |
| Comparative Tracking Index | 175 - 203 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 31 - 47 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 - 60.4 | °C | |
| Middle Temperature | 73.8 - 74.1 | °C | |
| Nozzle Temperature | 87.8 - 88.0 | °C | |
| Processing (Melt) Temp | 107 - 164 | °C | |
| Mold Temperature | 173 - 177 | °C | |
| Injection Pressure | 8.60 - 175 | MPa | |
| Holding Pressure | 59.8 | MPa | |
| Back Pressure | 0.207 - 10.0 | MPa | |
| Screw Speed | 50 - 60 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Phenolic - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecopet® PT70 GR30 NL100 PR | Eurotec Engineering Plastics | PET | Tecopet® |
| Tarnoform® 300 EC2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| DynaStat® 157 | Polymer Dynamix | TPO | DynaStat® |
| Hostacom BJ62A | LyondellBasell Industries | PP Copolymer | Hostacom |
| Huafon JF-W-3300A | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |