Electroblend® PBT-1901
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Electroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AymPUx_Electroblend-PBT-1901.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Electroblend® PBT-1901 is a glass fiber reinforced antistatic polybutylene terephthalate compound characterized by high mechanical with lower shrinkage properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 7200 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+8 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 240 to 245 | °C | |
| Middle Temperature | 245 to 250 | °C | |
| Front Temperature | 250 to 255 | °C | |
| Nozzle Temperature | 255 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-1170M | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Calprene® H6174 | Dynasol Elastomers | SEBS | Calprene® |
| Axiall PVC 5006 Natural | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Formolene FORMAX® L71709E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| GLAMIDE® T-663G50A | TOYOBO America, Inc. | PARA | GLAMIDE® |