NEXUS BIO BIO-200
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AyBqOX_NEXUS-BIO-BIO-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Grade Biodegradable Starch Resin Nexus BIO-200 are granules in light yellow and come in cylindrical and round shape with slight fragrance. They absorb moisture easily and are easily decomposed by microbes. They are anti-static. The processing temperature of the granules is lower than that of conventional plastic. They are easily colored. Such resin can be processed into finished products alone without adding any other polyolefin materials like PE, PP, PVA, PVA, EVA, etc. Applications include being directly molded into finished products. Its melt flow rate is high. It is suitable to make all kinds of containers, like plant nursery pots and bowls, soya bean curd trays, agricultural pesticide bottles, shampoo and shower gel bottles, straws, toys, packaging boxes, and all sorts of disposable containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 to 1.10 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) | 2.0 to 5.0 | g/10 min | Internal Method |
| Moisture Content | 0.30 to 1.2 | % | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 70 | % | Internal Method |
| Degradation Rate - in 100 days | > 46 | % | ISO 14855:2000 |
| Hexane Extraction | < 4.0 | % | Internal Method |
| Thermal Shrinkage | < 2.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 50 | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | > 20.0 | MPa | Internal Method |
| Tensile Elongation (Break) | > 50 | % | Internal Method |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 20 | kJ/m² | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 85.0 | °C | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNIGARD™ HP HFDA-1544 NT | The Dow Chemical Company | PE Copolymer | UNIGARD™ |
| Adsyl 3 C 30 F HP | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Fortron® 6165A6 | Celanese Corporation | PPS | Fortron® |
| LightSpan® LS1-6140 | NuSil Technology | Silicone | LightSpan® |
| Moplen EP542R | PolyMirae | PP Impact Copolymer | Moplen |