Toughblend® PBT-1200
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Toughblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AxfQ50_Toughblend-PBT-1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughblend® PBT-1200 is a glass fiber reinforced compound; offering good mechanical and thermal properties, with additional good chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 87.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 4100 | MPa | ASTM D790 |
| Flexural Strength | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 215 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 195 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 240 to 245 | °C | |
| Middle Temperature | 245 to 250 | °C | |
| Front Temperature | 255 to 260 | °C | |
| Nozzle Temperature | 255 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-1950-50A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Cadence™ GS5 | Eastman Chemical Company | Copolyester | Cadence™ |
| LEXAN™ ML7682 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ LUBRICOMP™ RFL22E compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Alpha PVC 2222RX-75 | Mexichem Specialty Compounds Inc. | PVC, Unspecified | Alpha PVC |