TORZEN® U4630HSL NC01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AxQmBe_TORZEN-U4630HSL-NC01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® U4630HSL NC01 is a heat-stabilized, lubricated molding grade PA66 in natural color. The heat stabilizer system has been designed to provide excellent property retention in high temperature applications. U4630HSL is also available in black. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.1 | % | |
| Flow : 2.00 mm | 2.1 | % | |
| Water Absorption (23°C, 24 hr) | 1.7 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 84.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.4 | % | |
| Break | 30 | % | |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 4.4 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (2.00 mm) | 10 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.710 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.710 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 750 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Screw Speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polyethylene E204-00 | RheTech, Inc. | HDPE | RheTech Polyethylene |
| VENYL VN007 - 8139 | AD majoris | Nylon 66/6 | VENYL |
| NILENE® E6 K20VA V0 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Durolon® VRY2500 | Unigel Plásticos | PC | Durolon® |
| INEOS PP R01A-00 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |