ForTii® XS81B
| Category: | Nylon 4T , Polyamide 4T |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | ForTii® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Aw9Mi0_ForTiiXS81B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ForTii®XS81B is a Polyamide 4T (Nylon 4T) material, which contains a 50% glass fiber reinforced material. This product is available in the Asia-Pacific region,. ForTii®The main characteristics of XS81B are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.63 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.45 | -- | % | ISO 294-4 |
| Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | 17000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 280 | 230 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 2.3 | % | ISO 527-2 |
| Flexural Modulus | 16500 | -- | MPa | ISO 178 |
| Flexural Stress | 380 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 315 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.5 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 325 - 335 | °C | |
| Front Temperature | 330 - 335 | °C | |
| Nozzle Temperature | 330 - 335 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 - 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 383 TFE 15 SI 2 | RTP Company | PC | RTP |
| ALCOM® PP 620/1 MR40 WT1060-12LB | ALBIS PLASTIC GmbH | PP, Unspecified | ALCOM® PP |
| APEX® 78-A447H-18 | Teknor Apex Company | PVC, Flexible | APEX® |
| Gallonprene® GP520-4504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kynar® 721 | Arkema | PVDF | Kynar® |