KOPLA PP KPE1030
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AvbUlb_KOPLA-PP-KPE1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PP KPE1030 is a Polypropylene material. It is available in Asia Pacific. Important attributes of KOPLA PP KPE1030 are:
Typical application of KOPLA PP KPE1030: Automotive |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.840 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 to 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 15.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 294 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 9.81 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 135 | °C | |
| 1.8 MPa, Unannealed | 75.0 | °C | |
| Melting Temperature | 163 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflex GM1810BE | LyondellBasell Industries | mLLDPE | Starflex |
| SureSpec HP-120NA | Genesis Polymers | PP Homopolymer | SureSpec |
| DESLOY™ DSC891A | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| LG PS 20HR(E) | LG Chem Ltd. | PS (HIPS) | LG PS |
| Telcar® TL-1431C | Teknor Apex Company | TPE | Telcar® |