HANWHA CLNA-8141SC
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AvEqRp_HANWHA-CLNA-8141SC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA Wire & Cable Compound CLNA-8141SC is a low density, crosslinkable polyethylene compound designed for high voltage (154kV and higher) power cable insulation requiring a high degree of cleanness. It has a extremely low level of contamination and proper balance of non-staining antioxidant and peroxide to ensure thermal stability and optimum cure levels. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Degree of Crosslinking | 82 | % | ASTM D2765A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | % | IEC 60811-2-1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 550 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (136°C, 168 hr) | < -5.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (136°C, 168 hr) | < -5.0 | % | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.28 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 4.0E-4 | ASTM D150 |
| Additional Information |
|---|
| Failures after 21 days:0 in 10% Igepal C 0 -6300 in 100% Igepal C 0 -630 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 115 - 130 | °C |
| Extrusion instructions |
|---|
| Cure Temperature : 300~390°CLine Speed : 2~3 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0336T30L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| BLUESTAR® 1110 | Nantong Xingchen Synthetic Material Co., Ltd. | PBT | BLUESTAR® |
| Grivory® HT1V-6 FWA black 9225 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| LEXAN™ 925 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 8377-75UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |