Ad-Tech Epoxy EA-622
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ad-Tech Plastic Systems Corp. |
| Trademark: | Ad-Tech Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Aud5QC_Ad-Tech-Epoxy-EA-622.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EA-622 ia a two-component paste compound with quick cure characteristics. The blue resin and yellow hardener when mixed together gives a uniform green color and provides a positive mix indicator. EA-622 will cure at temperatures as low as 0°F. It exhibits an easy 1 to 1 mix ratio with a working life of 15-20 minutes at 25°C/77°F, and sets to handling strength in 30-45 minutes. Typical applications: All types of general repair and bonding applications. EA-622 offers a quick, easy repair of similar and dissimilar materials. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6350 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 16.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.7 | % | ASTM D638 |
| Flexural Modulus | 1640 | MPa | ASTM D790 |
| Flexural Strength (Break) | 25.9 | MPa | ASTM D790 |
| Compressive Modulus | 945 | MPa | ASTM D695 |
| Compressive Strength | 38.7 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 33.0 | °C | |
| 1.8 MPa, Unannealed | 28.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 100 | wk | |
| Post Cure Time (25°C) | 0.50 to 0.75 | hr |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Lap Shear - Aluminum/Aluminum | 14.7 | MPa | ASTM D1002 |
| Work Life (25°C) | 16.0 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softflex® 0809 | Network Polymers, Inc. | TPE | Softflex® |
| Diaterm® A27 10 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |
| Eltex® P KS341 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Sylvin 8250-80LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Fortron® 1132L4 | Celanese Corporation | PPS | Fortron® |