SORVEX 1100
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Sorensen Ventures |
| Trademark: | SORVEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AuS7Qi_SORVEX-1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SORVEX 1100 is a Polybutylene Terephthalate (PBT) product. It is available in North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 to 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 4.0 to 9.0 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Color b | < 4.00 | ||
| Color L | > 85.0 | ||
| Intrinsic Viscosity | 1.2 to 1.3 | dl/g | ASTM D2857 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Carboxyl End Groups | 33.0 to 40.0 | meq/kg |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 to 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 49.0 to 58.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 200 | % | ASTM D638 |
| Flexural Modulus | 2260 | MPa | ASTM D790 |
| Flexural Strength | 78.5 to 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | > 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 155 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| Melting Temperature | 223 to 227 | °C | DSC |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | > 20 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.30 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ TH-418.S001 6770 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| SAXALEN™ PPH329B20 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| SLOVAMID® 6 CF 20 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Sup-tech A101 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| ELASTOSIL® LR 3043/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |