LNP™ LUBRICOMP™ IL004 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Au8Ug5_LNPLUBRICOMPIL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP IL004 is a compound based on Nylon 6/12 resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound IL-4040 Product reorder name: IL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.7 - 1.9 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.7 - 1.9 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.8 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.8 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2190 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2 |
| Fracture | 47.6 | MPa | ASTM D638 |
| Fracture | 49.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 14 | % | ASTM D638 |
| Yield | 15 | % | ISO 527-2 |
| Fracture | 14 | % | ASTM D638 |
| Fracture | 16 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.25 | ASTM D3702 Modified | |
| With Self-Static | 0.27 | ASTM D3702 Modified | |
| Wear Factor - Washer | 18.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.10 | J | ASTM D3763 |
| -- | 0.500 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 158 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 155 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 61.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 64.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 254 - 266 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 615 NP | Custom Resins Group | Nylon 6 | Nylene® |
| Axpoly® r-PP52 1000 | Axion Polymers | PP Copolymer | Axpoly® |
| HiFill® PEEK GF30 A 2020 | Techmer Engineered Solutions | PEEK | HiFill® |
| Kumho EP HAB 8710NH | Korea Kumho Petrochemical Co., Ltd. | ABS+PBT | Kumho EP |
| Sylvin 8685-60 Orange 583 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |