SABIC® LLDPE 218BJ Datasheet,LLDPE,Saudi Basic Industries Corporation (SABIC)-SHANGHAI SUSHENG

SABIC® LLDPE 218BJ

Wechat: WECHAT

Message
SABIC® LLDPE 218BJ is a butene linear low density polyethylene resin with an additive package typically designed for a broader range of food applications (TNPP free). The good thermal stability allows to use the resin in critical extrusion processing conditions. Films produced from SABIC® LLDPE 218BJ have better draw-down ability compared to lower MFR LLDPE resins. SABIC® LLDPE 218BJ is a Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 218BJ contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It also exhibits good Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements. For jacketing applications, addition of Carbon Black or UV stabilizer is required. Applications Blown Film: SABIC® LLDPE 218BJ is typically used for food applications (lamination film, barrier film) but can also be used in industrial packaging and as blending partner with other SABIC® PE resins in both blown and cast film applications. SABIC® LLDPE 218BJ is typically used for food applications (lamination film, barrier film) and pallet hand wrap. Masterbatch Compounding: It is suitable for additive masterbatches (eg. slip agents, anti fog agents, anti static agents, thermal stabilizers) in film and blow moulding applications. Wire & Cable Extrusion: Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. This product is not intended for and must not be used in any pharmaceutical/medical applications.

Message

SABIC® LLDPE 218BJ is a butene linear low density polyethylene resin with an additive package typically designed for a broader range of food applications (TNPP free). The good thermal stability allows to use the resin in critical extrusion processing conditions. Films produced from SABIC® LLDPE 218BJ have better draw-down ability compared to lower MFR LLDPE resins.

SABIC® LLDPE 218BJ is a Linear Low Density Polyethylene natural resin typically used for wire and cable applications.

SABIC® LLDPE 218BJ contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It also exhibits good Environmental Stress Crack Resistance (ESCR).

Sufficient Cu-inhibitor should be added to meet specific ageing requirements. For jacketing applications, addition of Carbon Black or UV stabilizer is required.

Applications

Blown Film: SABIC® LLDPE 218BJ is typically used for food applications (lamination film, barrier film) but can also be used in industrial packaging and as blending partner with other SABIC® PE resins in both blown and cast film applications.

SABIC® LLDPE 218BJ is typically used for food applications (lamination film, barrier film) and pallet hand wrap.

Masterbatch Compounding: It is suitable for additive masterbatches (eg. slip agents, anti fog agents, anti static agents, thermal stabilizers) in film and blow moulding applications.

Wire & Cable Extrusion:

Telecommunication and Power cable (LV, MV, HV) jacketing.

Halogen-free flame retardant (HFFR) compounds.

One-step or two-steps silane crosslinkable for cable insulation.

This product is not intended for and must not be used in any pharmaceutical/medical applications.

General Information
Additive	Antioxidation
Features	Good ESCR (Stress Crack Resist.) Low density Butene comonomer Antioxidation Thermal stability, good Compliance of Food Exposure
Uses	Blown Film Jacketing Packaging Films Cable sheath Wire and cable applications Non-specific food applications Composite Industrial application Mixing Insulating material cast film Masterbatch
Appearance	Natural color
Processing Method	Blow film Wire & Cable Extrusion Composite cast film

Physical	Nominal Value	Unit	Test Method
Density	0.918	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	48		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	12.0	MPa	ASTM D638
Fracture	17.0	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	16	%	ASTM D638
Fracture	790	%	ASTM D638
Flexural Modulus - 1% Secant	254	MPa	ASTM D790

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	20	µm
Elastic Recovery - Cast Film (20.0 µm)	53	%	ASTM D5459
Protrusion Puncture Resistance - Cast Film (20.0 µm)	2.20	J	ASTM D5748
Retention Force - 60 sec (20.0 µm) ¹	970	g
Stress Retention - Cast Film (20.0 µm)	80	%	ASTM D5459
Ultimate Pre-stretch Level - Cast Film (20.0 µm)	310	%

Additional Information	Nominal Value	Unit	Test Method
Dart Impact - Cast Film (20.0 µm)	28.0	J/cm	ISO 7765-2
Peel Cling ²			ASTM D5458
0% pre-stretch : 20.0 µm	153.0	g/2.5 cm	ASTM D5458
200% pre-stretch : 20.0 µm	127.5	g/2.5 cm	ASTM D5458
Tear strength- TD (20.0 µm) ³	185.0	kN/m	ISO 6383-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	96.0	°C	ISO 306/A
Melting Temperature (DSC)	122	°C	Internal method

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	5.0E+15	ohms·cm	ASTM D257
Dielectric Strength ⁴	55	kV/mm	ASTM D149
Dielectric Constant (60 Hz)	2.17		ASTM D150
Dissipation Factor (60 Hz)	1.0E-3		ASTM D150

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 20.0 µm, Cast Film)	92		ASTM D2457
Haze (20.0 µm, Cast Film)	1.2	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Cast FilmProperties are determined on 20µm cast stretch film produced on a 2m commercial cast stretch line: melt temperature 270°C, chill roll temperature 20°C and line speed of 450 m/min.

Extrusion	Nominal Value	Unit
Melt Temperature	250 - 300	°C

Note Message
1 .	Cast Film
2 .	Cast Film
3 .	Cast Film
4 .	500 V/sec

Resin Grade	Manufacturer	Category	Trademark
Rhelon F2038H-01	RheTech, Inc.	Nylon 66	Rhelon
Rotec® ABS 3001 M	ROMIRA GmbH	ABS	Rotec® ABS
Trexprene® A64BI	Mitsubishi Chemical Performance Polymers, Inc.	TPV	Trexprene®
KPOL-NYLON K-NY66/21VCF	KPOL Chem Co.	Nylon 66	KPOL-NYLON
LNP™ THERMOCOMP™ DF003E compound	SABIC Innovative Plastics	PC	LNP™ THERMOCOMP™

Resin Grade

Manufacturer

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Au8FNQ_SABICLLDPE218BJ.pdf
PRICE:	Order Products email sales@su-jiao.com