Iupilon® TMB1615
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Au3fg6_Iupilon-TMB1615.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® TMB1615 is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® TMB1615 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.15 to 0.35 | % | |
| Flow : 3.20 mm | 0.15 to 0.35 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 67.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.8 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 4600 | MPa | ISO 178 |
| Flexural Stress | 108 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 150 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 210 to 250 | °C | |
| Middle Temperature | 220 to 260 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 230 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 30 to 50 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205F TFE 15 | RTP Company | Nylon 12 | RTP |
| Spartech Polycom SCR1-5005F | Spartech Polycom | ABS | Spartech |
| Estane® 58226 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| INEOS PP 100-GB06 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| INVISION™ VX 5065UI | A. Schulman Inc. | TPV | INVISION™ |