Bergamid™ B70 G/GK30 TM-Y UV NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AtC8Fl_Bergamid-B70-G-GK30-TM-Y-UV-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6016158 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 2(23°C, 4.00 mm, Injection Molded) | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 5400 | MPa | ISO 527-2/1 |
| Tensile Strength 3(23°C, 4.00 mm) | 90.0 | MPa | ISO 527 |
| Tensile Elongation 4(Break, 23°C, 4.00 mm) | 3.0 | % | ISO 527 |
| Flexural Modulus (23°C) | 4100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 6.5 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C, Injection Molded | 55 | kJ/m² | |
| 23°C, Injection Molded | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 205 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 190 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm, ALL) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.03 |
| 2 . | Bergmann Method |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVALON® 85 AE | Huntsman Corporation | TPU-Polyester | AVALON® |
| Epoxies, Ect. 20-2390 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| Hanwha Total PP RB210 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina IVORY PVC COMPOUND ML-850-WK-IS-FLEX (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST XU 150BB11 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |