PRL PC/TP-FR2
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AsGGaY_PRL-PC-TP-FR2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC/TP-FR2 is a Polycarbonate + Polyester (PC+Polyester) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 5.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 50.3 | MPa | |
| Break, 3.18 mm | 48.3 | MPa | |
| Flexural Modulus (3.18 mm) | 2000 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 370 | J/m | |
| 23°C, 3.18 mm | 690 | J/m | |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 90.6 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C | |
| RTI Elec (1.50 mm) | 75.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 75.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 75.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Processing (Melt) Temp | 246 to 274 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3035 JU5 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| NILENE® P25 K25BE | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| CERTENE™ LLHG-1522A | Muehlstein | LLDPE | CERTENE™ |
| HANWHA LLDPE 7635 | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| KPOL-LDPE LD K-1.20/920 | KPOL Chem Co. | LDPE | KPOL-LDPE |