GAZOLE™ 6430GF
| Category: | PBI , Polybenzimidazole |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | GAZOLE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ar0lGh_GAZOLE-6430GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high performance thermoplastic polymer, 30% glass fiber reinforced in PBI PEK Blend, semi-crystalline granules suitable for injection molding as well as extrusion, easy flow, dark green in color. Application Areas: Suitable for high temperature applications under extremely high load, Excellent wear resistance, suitable for semiconductor applications and plasma handling equipments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | |
| Molding Shrinkage 1 | |||
| Flow | 0.20 | % | |
| Across Flow | 0.58 | % | |
| Water Absorption (Equilibrium) | 0.24 | % | ASTM D570 |
| Spiral Flow 2 | 4.50 | cm | ASTM D3123 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weight Loss on Heating | Internal Method | ||
| 5% Weight Loss in Air | 580 | °C | |
| 5% Weight Loss in Nitrogen | 570 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (A-Scale) | 30 | ASTM D785 | |
| Durometer Hardness (Shore D) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 13500 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 167 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.7 | % | ASTM D638 |
| Flexural Modulus (23°C) | 13600 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 282 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 310 | °C | ASTM D648 |
| Continuous Use Temperature | 300 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 445 | °C | |
| Processing (Melt) Temp | 400 to 445 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 445°C nozzle, 220°C Mold |
| 2 . | 445°C nozzle, 220°C Mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 GB 20 | RTP Company | PESU | RTP |
| TEKAFIN™ PB50GM | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| Desmoderm® KE 072 | Covestro - PUR | PUR-Ether | Desmoderm® |
| Devcon Plastic Welder™ II | Devcon | Epoxy | Devcon |
| Karina WHITE PVC COMPOUND -E 836-10/176-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |