Starpylen MFB44S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Aql1Yx_Starpylen-MFB44S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen MFB44S is a glass Beads, Glass Fiber Reinforced, Polypropylene Injection Molding Resin heat stabilised( also known as Starpylen WS 2020VK S37.7 ) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 3.00 to 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (4.00 mm) | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4200 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 74.0 | MPa | |
| -- 4 | 65.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact Strength 5(23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 125 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF10 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Toppyl SP 2000 B | LyondellBasell Industries | Polyolefin, Unspecified | Toppyl |
| Delta PPR-1G30 | Delta Polymers | PP Homopolymer | Delta |
| LUVOCOM® 80-7580 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Durethan® DP 2325 H3.0 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |