LNP STAT-KON WS002I is a compound based on Polybutylene Terephalate resin containing Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. Also known as: LNP* STAT-KON* Compound WS-HI Product reorder name: WS002I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 1.6 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 36.5 | MPa | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 138 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+6 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UmaPET HQIM | Ester Industries Ltd. | PET | UmaPET |
| Amodel® AT-1125 HS | Solvay Specialty Polymers | PPA | Amodel® |
| Forflex® 71600ID42 | SO.F.TER. SPA | TPO (POE) | Forflex® |
| Pearlthane® 11T98 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| POLYfill PP CCP20020 UV | Polykemi AB | PP, Unspecified | POLYfill |