Badamid® PA612 GF33
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AoGeDz_Badamid-PA612-GF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® PA612 GF33 is a Polyamide 612 (Nylon 612) material filled with 33% glass fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA612 GF33: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 9500 | 7900 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 168 | 140 | MPa | ISO 527-2/1A/5 |
| Tensile Strain 3(Break, 23°C) | 3.0 | 3.2 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 218 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| Glow Wire Flammability Index (0.750 to 1.60 mm) | 675 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.750 to 1.60 mm) | 700 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 V20 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Sinvicomp SIZ5908A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| NANCAR® 1051 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| ADDINYL C2 ZV40 | ADDIPLAST | Nylon 66/6 | ADDINYL |
| Sylvin 9604-90 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |