AKROMID® B3 GF 30 9 RM-M natural (3292)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AmvKw8_AKROMID-B3-GF-30-9-RM-M-natural-3292-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 30 9 RM-M natural (3292) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength, limited moisture absorption and light inherent color. Applications are housings and other dimensional stable parts in the automotive and electronic industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.41 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 70.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.40 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.6 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 3.2 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 230 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 170 | 115 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | 4.2 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 9600 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 60 | kJ/m² | |
| 23°C | 70 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 160 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 225 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® AG2677 | Covestro - Polycarbonates | PC | Makrolon® |
| Shandong PA1212 PA1212BR-III | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| VITAMIDE® BK70BK6683 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| NILAMID® A3 GB20 | Nilit Plastics | Nylon 66 | NILAMID® |
| Formolene® 2575N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |