TRANSMARE® 19HGF30-1.003
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AmkodA_TRANSMARE-19HGF30-1-003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HGF30-1.003 is a black colored 30% glass fiber reinforced polypropylene homopolymer for injection molding purposes with very high stiffness and a good flow. This grade does not contain any traces of polyethylene. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.5 | g/10 min | |
| 230°C/5.0 kg | 25 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 5700 | MPa | ISO 178 |
| Flexural Stress 2(Injection Molded) | 133 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C, Injection Molded | 8.3 | kJ/m² | |
| -20°C, Injection Molded | 8.5 | kJ/m² | |
| 0°C, Injection Molded | 9.0 | kJ/m² | |
| 23°C, Injection Molded | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -30°C, Injection Molded | 45 | kJ/m² | |
| 23°C, Injection Molded | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C, Injection Molded | 10 | kJ/m² | |
| -20°C, Injection Molded | 10 | kJ/m² | |
| 0°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | 12 | kJ/m² |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Charpy Unnotched Impact Strength - Injection Molded | ISO 188 | ||
| -30°C | 22 | % | |
| 23°C | 3.0 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 154 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIC3704AUV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Bergamid™ A70 G15 H BK013 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Elastron® G G101.A58.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Ketron® PEEK-GF30 | Quadrant Engineering Plastic Products | PEEK | Ketron® |
| Karina BLACK PVC COMPOUND 951-48/4-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |