Generic PC Alloy - Glass Fiber
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Al0Zf5_Generic-PC-Alloy---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC Alloy - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 - 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.25 - 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 83 - 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 54.0 - 125 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 7.0 - 18 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2960 - 12000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 92.0 - 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 76 - 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 142 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 - 138 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 - 1.0E+16 | ohms | ASTM D257 |
| Dielectric Strength (23°C) | 19 - 22 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 115 | °C | |
| Drying Time | 3.5 - 3.6 | hr | |
| Rear Temperature | 240 - 259 | °C | |
| Middle Temperature | 248 - 302 | °C | |
| Front Temperature | 255 - 302 | °C | |
| Processing (Melt) Temp | 248 - 266 | °C | |
| Mold Temperature | 105 - 110 | °C | |
| Back Pressure | 0.613 - 0.725 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC Alloy - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Abstron HI40H | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Bayfill® EA 2003 (5 pcf) | Covestro - PUR | PUR-Ether/MDI | Bayfill® |
| Fainplast PVC GK 83 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LEXAN™ HP2R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Durethan® C 38 FAM 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |