LNP™ LUBRILOY™ D20009 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AkkWTN_LNPLUBRILOYD20009compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D20009 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant. Also known as: LNP* LUBRILOY* Compound D-FR Product reorder name: D20009 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 61.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 84 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 87.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.25 | ASTM D3702 Modified | |
| With Self-Static | 0.13 | ASTM D3702 Modified | |
| Wear Factor - Washer | 56.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 700 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-2 | UL 94 | |
| 3.00 mm, Testing by SABIC | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASI POLYPROPYLENE 1404-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| FHR Polypropylene P5M6K-048 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Flontech® FT-EK10-3 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Karina GREEN COLOR CONCENTRATE 40/ 86-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ULTEM™ 1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |