4MID® 9A22120
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | 4Plas |
| Trademark: | 4MID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AkHDd3_4MID-9A22120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4MID®9A22120 is a polyamide 66 (nylon 66) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6300 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 240 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 255 | °C | ISO 306/B |
| Melting Temperature 2 | 262 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | < 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 A FR UV | RTP Company | Nylon 6 | RTP |
| SLOVALEN® PH 91 C 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| Daelim Po1y® PP-333 | DAELIM INDUSTRIAL CO., LTD. | PP Random Copolymer | Daelim Po1y® |
| Desmopan® DP 6080A | Covestro - PUR | TPU, Unspecified | Desmopan® |
| TOTAL Polyethylene HDPE SB 1359 NA | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |