Ultramid® 8202
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AkGYgu_Ultramid-8202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8202 is a low viscosity, general purpose PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ultramid 8202 HS) and/or pigmented versions. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance. Applications Ultramid 8202 is generally recommended for applications such as gears, fittings, casters, beatings, clips, fasteners, plugs, caps, and filter bowls. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| Saturation | 9.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 9.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.7 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 2700 | 970 | MPa | |
| 80°C | 485 | 550 | MPa | |
| 121°C | 360 | 320 | MPa | |
| Tensile Strength | ||||
| Yield, -40°C | 126 | 110 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 79.0 | 36.0 | MPa | ASTM D638 |
| Yield, 80°C | 35.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 121°C | 25.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 78.0 | 36.0 | MPa | ISO 527-2 |
| Break, 23°C | 75.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 16 | % | ASTM D638, ISO 527-2 |
| Yield, 80°C | 42 | 35 | % | ASTM D638 |
| Yield, 121°C | 36 | 40 | % | ASTM D638 |
| Break, 23°C | 55 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 3010 | 3660 | MPa | ASTM D790 |
| 23°C | 2830 | 740 | MPa | ASTM D790 |
| 65°C | 500 | -- | MPa | ASTM D790 |
| 90°C | 350 | -- | MPa | ASTM D790 |
| 121°C | 305 | -- | MPa | ASTM D790 |
| 23°C | 2400 | 770 | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 170 | 154 | MPa | ASTM D790 |
| 23°C | 108 | 35.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 90°C | 20.0 | -- | MPa | ASTM D790 |
| 121°C | 17.0 | -- | MPa | ASTM D790 |
| 23°C | 85.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 51 | -- | kJ/m² | |
| 23°C | No Break | -- | ||
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 48 | 43 | J/m | |
| 23°C | 58 J/m | No Break | ||
| Drop Impact Resistance (23°C) | 142 | > 271 | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 178 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 8.3E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| 6.00 mm | 125 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| 6.00 mm | 75.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C | |
| 6.00 mm | 85.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | ||||
| 1.50 mm 1 | 22 | -- | kV/mm | ASTM D149 |
| -- | 37 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 100 Hz | 3.50 | -- | ||
| 1 MHz | 3.30 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.010 | -- | ||
| 1 MHz | 0.020 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| 6.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 805CC SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| TAIRILAC AG22AT | Formosa Plastics Corporation | ABS | TAIRILAC |
| VICOTE® F807Blk | Victrex plc | PEEK | VICOTE® |
| Colorite 77 Series 8077 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |
| Karina IVORY PVC COMPOUND -E 75901-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |