CABELEC® CA6141
| Category: | PC , Polycarbonate |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AkE0Bv_CABELEC-CA6141.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 6141 is an electrically conductive compound based on conductive carbon black dispersed in a modified polycarbonate. CABELEC® 6141 has been specially formulated for injection moulding applications. It has been developed to give a balanced property profile with permanent electrical conductivity. CABELEC® 6141 is recommended for packaging and electronic product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosive powders, pigments and electronic components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.20 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 260°C/10.0 kg | 12 | g/10 min | |
| 260°C/2.16 kg | 0.60 | g/10 min | |
| 260°C/5.0 kg | 4.0 | g/10 min | |
| Molding Shrinkage - Flow 3 | 0.70 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 4(Shore D, 15 sec) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5 | ISO 527-2 | ||
| Yield | 54.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Strain 6(Break) | 24 | % | ISO 527-2 |
| Flexural Modulus 7 | 2170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 8(23°C) | 22 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9(1.8 MPa, Unannealed) | 121 | °C | ISO 75-2/A |
| Vicat Softening Temperature 10 | 149 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | 1.0E+5 | ohms | Internal Method |
| Volume Resistivity 12 | 2.0E+2 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Middle Temperature | 270 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E047 |
| 4 . | CTM E030 |
| 5 . | CTM E041 |
| 6 . | CTM E041 |
| 7 . | CTM E040A |
| 8 . | CTM E044A |
| 9 . | CTM E038 |
| 10 . | CTM E039 |
| 11 . | CTM E042E |
| 12 . | CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001 | PolyOne Corporation | PC | Stat-Tech™ |
| Hyundai EP Adhesives LE340T/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| LEXAN鈩?243R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Lucky Enpla LGF5408 | Lucky Enpla Co LTD | Nylon 6 | Lucky Enpla |
| POCAN® T 7323 000000 | LANXESS GmbH | PBT+PET | POCAN® |