ASTALON™ S3000
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AiUI86_ASTALON-S3000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALON™ S3000 / S3001 / S3003 are the standard low/medium viscosity (high melt flow) grades in the ASTALON™ range and are suited to general purpose injection moulding applications. Offering an exceptional combination of transparency, toughness, heat resistance, flame retardancy and processability, typical applications include food processors and other kitchen appliances, serving trays, electrical power tool housings, medical dialysis components and central heating floor ducts. Note: [ Standard grade = S3000 ] / [ FDA approved = S3001 ] / [ Steam resistant = S3003 ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 63.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 110 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 830 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | > 85.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 152 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 137 | °C | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | 2.85 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 85.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 235 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 265 to 285 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® A2 500350M | ELASTO | SEBS | Mediprene® |
| Sylvin 8201-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| FORMULA P COMP 7210 Z2 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| K-Bin Rigid PVC KB-6401 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| LEXAN™ 923A resin | SABIC Innovative Plastics | PC | LEXAN™ |