AKROMID® B3 GF 30 S1 white (3767)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AiFHg7_AKROMID-B3-GF-30-S1-white-3767-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 30 S1 white (3767) is a 30% glass fibre reinforced, cold impact strength polyamide 6 with high stiffness and strength Applications are housings and covers for the automotive industry and power tools |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7700 | MPa | ISO 178 |
| Flexural Stress 2 | 250 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 4.5 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 30 | % | ISO 1172 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | |
| 23°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 145 | °C | ISO 75-2/C |
| Melting Temperature 4 | 220 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren N110 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Miramid® VE25CW | BASF Leuna GmbH | Nylon 6 | Miramid® |
| NILAMID® B3 D | Nilit Plastics | Nylon 6 | NILAMID® |
| 3SP™ E-Denstone Peach | EnvisionTEC, Inc. | Unspecified | 3SP™ |
| Formolene® 5140N | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |