QAMAR CD18N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SPDC Ltd. |
| Trademark: | QAMAR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AhuEQS_QAMAR-CD18N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
QAMAR CD18N is a linear low density polyethylene material,. This product is available in North America, Africa and the Middle East, Europe or Asia Pacific. The processing method is: cast film. The main characteristics of QAMAR CD18N are: high liquidity. The typical application fields of QAMAR CD18N are: movies |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ISO 1872-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 9.00 | MPa | ISO 1872-2 |
| Tensile Strain (Break) | > 430 | % | ISO 1872-2 |
| Flexural Modulus | 200 | MPa | ISO 1872-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 30 µm | 190 | MPa | ISO 527-3 |
| TD : 30 µm | 210 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 30 µm | 35.0 | MPa | ISO 527-3 |
| TD : Break, 30 µm | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 30 µm | 600 | % | ISO 527-3 |
| TD : Break, 30 µm | 900 | % | ISO 527-3 |
| Dart Drop Impact (30 µm) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 30 µm | 30 | N | ISO 6383-2 |
| TD : 30 µm | 120 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ISO 974 |
| Vicat Softening Temperature | 99.0 | °C | ISO 306 |
| Melting Temperature | 122 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 12 | % | ISO 14782 |
| Extrusion instructions |
|---|
| Resin Temperature: 180°CBlow up ratio: 2.0Extruder: 40mm, L/D=24Die Diameter: 75mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer S40H | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| Spartech Polycom X02474 | Spartech Polycom | PP Homopolymer | Spartech |
| Bayblend® ET3036 FR | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Glastic® 1125 | Glastic Corporation | Polyester, TS | Glastic® |
| HiFill FR® PC NR 06 NAT | Techmer Engineered Solutions | PC | HiFill FR® |