FRIANYL® A3 GF35 V0P1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AgcHWI_FRIANYL-A3-GF35-V0P1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRIANYL® A3 GF35 V0P1 is a Polyamide 66 (Nylon 66) compound, 35% glass fiber reinforced, flame retardant with red phosphorous and low phosphate release, UL listed V0. This compound is intended for injection molding. FRIANYL® A3 GF35 V0P1 is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.70 | % | |
| Flow : 23°C | 0.50 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.60 | % | |
| Saturation, 23°C | 4.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | 45 | kJ/m² | |
| 30°C | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 9.5 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 248 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 125 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 21 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | V | IEC 60112 |
| Needle Flame Test | IEC 60695-11-5 | ||
| 1.00 mm | Pass | ||
| 2.00 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm, NC | V-1 | ||
| 0.800 mm, BK | V-0 | ||
| 1.60 mm, NC, Bk | V-0 | ||
| 3.20 mm, NC, BK | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 3.20 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | |
| 3.20 mm | 825 | °C | |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Flammability 3 | SE | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| 3 . | 355x100x1mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® AER003N | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| Santoprene™ 123-52W242 | ExxonMobil Chemical | TPV | Santoprene™ |
| EGYPTENE LL 0209 AA | Sidpec (Sidi Kerir Petrochemicals Co.) | LLDPE | EGYPTENE |
| ESENTTIA 06C30DA | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| LG PMMA HI855S | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |