RIALFLAME C V0S 02 S 20 T0
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFLAME |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Agbz1F_RIALFLAME-C-V0S-02-S-20-T0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound 20% talc filler, flam retardant; classifiable, according to the norms of UL-94, V-0 up to 1.5mm. Main properties: retarding to the flame with extinction contained time; high flowability; good impact strength up to low temperatures and dimensional stability. Good characteristic as Glow Wire Specific flowability for extrusion, available in the version natural and colored. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 1.1 | % | |
| Ash Content | 20 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Test | Pass | IEC 60695-2-12 | |
| Needle Flame Test 1(2.00 mm) | Pass | IEC 60695-2-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 22.0 | MPa | |
| Break, 23°C | 18.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 200 | % | |
| Flexural Modulus 2(23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 2.7 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Ball Pressure Test | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index 3 | 28 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Melt Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Method A-B |
| 2 . | 2.0 mm/min |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC43P250-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Tarnoform® 210 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Alpha PVC GW 2326-A-VW1 NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Celstran® PP-GF40-0414 P7/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Eporex® 500 | Eternal Plastics Co., Ltd. | PS (GPPS) | Eporex® |