Order Products : sales@su-jiao.com
Hostaform® M90XAP®
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ag8zhq_Hostaform-M90XAP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® acetal copolymer grade M90 XAP® is a low emission version, medium viscosity polymer providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performance in many applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.8 | % | ISO 294-4 |
| Flow direction | 1.8 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.5 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2560 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.4 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Melting Temperature 1 | 167 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 165 - 175 | °C | |
| Middle Temperature | 170 - 180 | °C | |
| Front Temperature | 170 - 180 | °C | |
| Nozzle Temperature | 180 - 190 | °C | |
| Processing (Melt) Temp | 180 - 190 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 175 to 185°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCUDIA® EVA PA-448 | REPSOL | EVA | ALCUDIA® EVA |
| Desmopan® DP 9648DU | Covestro - PUR | TPU-Polyether | Desmopan® |
| FERREX® GPP30RA03HB | Ferro Corporation | PP, Unspecified | FERREX® |
| Formolene® 6520N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Karina IVORY PVC COMPOUND -E 650-35/1-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |