SOLLAMID A 2750 FV
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ag68bP_SOLLAMID-A-2750-FV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLLAMID A 2750 FV is a Polyamide 66 (Nylon 66) material filled with glass fiber. It is available in Latin America for injection molding. Primary attribute of SOLLAMID A 2750 FV: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.33 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 0.90 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ASTM D570 |
| Heat Stability | 100 to 120 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | 120 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 7500 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 160 | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | 7.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8500 | 5500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 260 | 200 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 25 | 18 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 230 | -- | °C | |
| 1.8 MPa, Unannealed | 230 | -- | °C | |
| Melting Temperature | 250 to 260 | -- | °C | |
| CLTE - Flow | 2.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 255 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP LGF 30 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Tenite™ Butyrate 580A3720016 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Mowiol® 26-88 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Nypol® PA A3 T30 PRTA010 NR380 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LOFEX® A311A | Lotte Chemical Corporation | PET | LOFEX® |