AKROMID® B3 3 S3 10 black 950063 (1809)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ag2Osx_AKROMID-B3-3-S3-10-black-950063-1809-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 3 S3 10 black 950063 (1809) is an unreinforced, nucleated, dry impact resistant polyamide 6 with light inherent color. Applications are handles and fittings for power tools and furniture industry. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 85.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.7 | -- | % | |
| Flow | 1.3 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.6 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 102 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2700 | 955 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 70.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.3 | 15 | % | |
| Break | > 45 | > 100 | % | |
| Flexural Modulus 1 | 2600 | 950 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | 10 | kJ/m² | |
| 23°C | 10 | 28 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 162 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min, DSC |
| 3 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130A90 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| Safrene® M 6650 | Safripol (PTY) LTD | HDPE | Safrene® |
| Rhelon M1020H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| omay® G21 | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |
| SQUARE® LIM2012-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |