ARLEN™ AE4200N
| Category: | Nylon 6T , Polyamide 6T |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | ARLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ae276f_ARLENAE4200N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ARLEN™AE4200N is a polyamide 6T (nylon 6T) material,. This product is available in North America,. ARLEN™The main features of the AE4200N are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.40 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00mm | 0.80 | -- | % | ASTM D955 |
| Transverse flow : 2.00mm | 1.0 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.30 | -- | % | ASTM D570 |
| 100°C, 24 hr | 2.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (2.00 mm) | 70.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 2.00 mm) | 4.0 | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3000 | 2700 | MPa | ASTM D790 |
| Flexural Strength | 120 | 110 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 70 | 80 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 145 | -- | °C | ASTM D648 |
| Glass Transition Temperature | 125 | -- | °C | DSC |
| Melting Temperature | 320 | -- | °C | |
| Linear thermal expansion coefficient | ASTM D696 | |||
| Flow | 6.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Lateral | 6.7E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 31 | -- | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | -- | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.014 | -- | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Hopper Temperature | 50 - 90 | °C | |
| Rear Temperature | 315 - 330 | °C | |
| Middle Temperature | 320 - 335 | °C | |
| Front Temperature | 325 - 340 | °C | |
| Nozzle Temperature | 325 - 340 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 150 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Medium Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL4F 802-SB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Maxelast® C4945E | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SABIC® PPcompound 8620A | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Texin® 260 | Covestro - PUR | TPU-Polyester | Texin® |
| Plasmer 8080N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |