WPP PP PPH2TF2-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AdebtZ_WPP-PP-PPH2TF2-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPH2TF2-Black is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 32.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/5 |
| Yield | 33.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 9.0 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 3 | 2300 | MPa | ASTM D790 |
| -- 4 | 2400 | MPa | ISO 178 |
| Flexural Stress 5 | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C | 3.0 | kJ/m² | ISO 180 |
| 23°C | 5.0 | kJ/m² | ISO 180/1B |
| Unnotched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 124 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 111 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 71.0 | °C | ASTM D648 |
| 1.8 MPa, annealed | 95.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® PJ9300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Trilliant™ HC X THC 1101 Natural | PolyOne Corporation | Copolyester | Trilliant™ HC |
| APEX® 07-U0296A-65 | Teknor Apex Company | PVC, Flexible | APEX® |
| Fiberfil® M-2501 BK | Fiberfil® Engineered Plastics Inc. | Nylon 66 | Fiberfil® |
| Durez® 33446 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |