Durethan® B 30 S FN40 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ad8x5z_DurethanB30SFN40000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ||||
| Vertical flow direction : 260°C, 2.00mm 1 | 0.90 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.30 | -- | % | ISO 294-4 |
| Flow direction : 260°C, 2.00mm 3 | 0.90 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.30 | -- | % | ISO 294-4 |
| Vertical flow direction : 260°C, 3.00mm 5 | 0.90 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 2 hours, 3.00mm 6 | 0.20 | -- | % | ISO 294-4 |
| Flow direction : 260°C, 3.00mm 7 | 0.90 | -- | % | ISO 2577 |
| Flow direction : 120°C, 2 hours, 3.00mm 8 | 0.20 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 10 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 135 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3400 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress | ||||
| Yield, 23°C | 90.0 | 45.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 60.0 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ||||
| Yield, 23°C | 4.0 | 23 | % | ISO 527-2/50 |
| Fracture, 23°C | 16 | 290 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 9.6 | 270 | % | ISO 527-2/50 |
| Flexural Modulus 9(23°C) | 3000 | 900 | MPa | ISO 178/A |
| Flexural Stress 10 | ||||
| 3.5% strain | 100 | 26.0 | MPa | ISO 178/A |
| 23°C | 120 | 35.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 11(23°C) | 5.9 | 8.1 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFR, 14-030; ISO 1043-PA FR (30) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | < 10 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 166 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 12 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index 13(Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 875 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 850 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | -- | °C | IEC 60695-2-13 |
| Oxygen Index 14 | 28 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 150x150x3; MT 80°C; 500 Bar |
| 6 . | 150x150x3 |
| 7 . | 150x150x3; MT 80°C; 500 Bar |
| 8 . | 150x150x3 |
| 9 . | 2.0 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | Pull Rate: 2 mm/min; 50% RH |
| 12 . | 10°C/min |
| 13 . | Erosion depth: 1.60mm |
| 14 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTADUR PBT | Röchling Sustaplast SE & Co. KG | PBT | SUSTADUR |
| Vitaster® US30WT6190 | Jackdaw Polymers | PBT | Vitaster® |
| ACCUTECH™ CP0436G5M25CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| ENVIROPLAS® ENV49-NC750 | ENVIROPLAS®, Inc. | PSU+PC | ENVIROPLAS® |
| SIBUR Synthetic Rubber SSBR-2560 TDAE Grade C | SIBUR | SBR, Solution | SIBUR Synthetic Rubber |