Pearlthane® 11T85
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AcwU9G_Pearlthane-11T85.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Aromatic Polycaprolactone Copolyester based Thermoplastic polyurethane Appearance: Colourless pellets Features: Medium hardness, excellent mechanical properties and easy processing. Application: Injection-moulding applications. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| 20°C | 1.16 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 20.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 6.00 | MPa | ASTM D412, ISO 527 |
| 300% strain | 10.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 640 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 90.0 | kN/m | ASTM D624 |
| -- | 90 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 35 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -45.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 178 - 188 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 195 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 35.0 | °C |
| Injection instructions |
|---|
| Clamping force: 50 tonsScrew diameter: 30 mmL/D ration: 23Maximum hydraulic pressure: 210 barMould: Plaque 120x120x2 mm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AECN TL | Arkema | Nylon 12 | Rilsan® |
| SABIC® PP 570P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| NuSil R-1082 | NuSil Technology | Silicone | NuSil |
| MAGNUM™ 3904 | Trinseo | ABS | MAGNUM™ |
| Eleme NGP250L | Eleme Petrochemical Company Ltd | PP Homopolymer | Eleme |