Salflex 255
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Acm9CL_Salflex-255.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Salflex 255 is a polyolefin thermoplastic elastomer (TPO (POE)) product,. It can be processed by blow molding or extrusion and is available in North America. The application fields of Salflex 255 include automobile industry and industrial application. The main characteristics are: impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.3 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.2 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 53 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 650 | % | ISO 527-2 |
| Flexural Modulus | 530 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 120 | kN/m | ISO 34-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -28°C | No Break | ISO 180/1A | |
| 23°C | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 62.0 | °C | ISO 75-2/B |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 75.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 2 Temp. | 180 - 225 | °C | |
| Cylinder Zone 3 Temp. | 180 - 225 | °C | |
| Cylinder Zone 4 Temp. | 180 - 225 | °C | |
| Melt Temperature | 180 - 230 | °C | |
| Die Temperature | 180 - 225 | °C |
| Extrusion instructions |
|---|
| Blow Molding Mold Temperature: 20 to 50°C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC501 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| SAXAMID™ 126F2K4 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Monprene® MP-3955B | Teknor Apex Company | TPE | Monprene® |
| TOTAL Polystyrene Compound 818E | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Karina IVORY PVC COMPOUND 807D35/ 1-C-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |