P-BLEND XS100
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | P-BLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ac5n4c_P-BLEND-XS100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS blend with excellent impact at -40°C and improved heat resistance, good UV-stability. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | ISO 527-2 |
| Fracture | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 100 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 33 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180 | ||
| -20°C | 15 | kJ/m² | ISO 180 |
| 23°C | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 50 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 265 - 270 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5233 B2 | Spartech Polycom | PP, Unspecified | Spartech |
| TORZEN® G3500HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| UNITAL® C | Nytef Plastics, Ltd. | Acetal (POM) Copolymer+PE | UNITAL® |
| LUVOCOM® 50-8779 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| WELLAMID Nylon 6600 GV 30 HYCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |